Active matrix electro-luminescent display device with an organic leveling layer

ABSTRACT

A resin material having a small relative dielectric constant is used as a layer insulation film. The resin material has a flat surface. A black matrix or masking film for thin film transistors is formed thereon using a metal material. Such a configuration prevents the problem of a capacity generated between the masking film and a thin film transistor.

This is a continuation of U.S. application Ser. No. 09/360,341, filedJul. 22, 1999, now U.S. Pat. No. 6,169,293, which is a continuation ofU.S. application Ser. No. 08/751,338, filed Nov. 18, 1996, now U.S. Pat.No. 5,952,708.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a configuration applicable to flatpanel displays represented by active matrix liquid crystal displays andEL type displays.

2. Description of Related Art

Conventional known flat panel displays include active matrix liquidcrystal displays having a configuration wherein a thin film transistorfor switching is provided to each of a number of pixels provided in theform of a matrix and wherein charge going in and out each pixelelectrode is controlled by the thin film transistor.

In such a configuration, a masking means (a light shielding means) mustbe provided to prevent light from entering the thin film transistorsprovided in a pixel region.

A metal film is currently chosen as the masking means (the lightshielding means) from the viewpoint of dispersion of impurities andstability. Further, such a masking means for thin film transistors isgenerally provided to serve also as a black matrix which coversperipheral edge regions of pixel electrodes.

Such a configuration has the following problems. The first problem isthat a capacity is generated between the masking film and the thin filmtransistors, and this adversely affects the operation of the thin filmtransistors. The second problem is that since the masking film isgenerally formed on a substrate having irregularity thereon which canmake the masking function insufficient.

The problem associated with the masking function equally applies to theblack matrix provided so as to overlap with the edges of pixels.

It is an object of the invention disclosed in this specification toprovide a configuration which solves the problems associated with amasking film for shading thin film transistors to achieve highperformance as an active matrix display.

SUMMARY OF THE INVENTION

A configuration according to the invention disclosed in thisspecification is characterized in that it comprises:

thin film transistors having outputs connected to pixel electrodes;

a layer insulation film made of a resin material provided on the thinfilm transistors; and

a masking film for shading the thin film transistors provided on thelayer insulation film.

Another configuration according to the present invention ischaracterized in that it comprises:

a layer insulation film made of a resin material formed on thin filmtransistors; and

a masking film for shading the thin film transistors formed on the layerinsulation film made of a resin material.

Still another configuration according to the present invention ischaracterized in that it comprises: a plurality of pixel electrodesprovided in the form of a matrix; and a black matrix for covering atleast a part of peripheral regions of the pixel electrodes, the blackmatrix being provided on a layer insulation film made of a resinmaterial.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A through 1D illustrate steps of producing a pixel portion of anactive matrix circuit.

FIGS. 2A through 2C illustrate steps of producing a pixel portion of anactive matrix circuit.

FIGS. 3A through 3C illustrate steps of producing a pixel portion of anactive matrix circuit.

FIGS. 4A through 4C illustrate steps of producing a pixel portion of anactive matrix circuit.

FIGS. 5A through 5D illustrate steps of producing a pixel portion of anactive matrix circuit.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENT

A first embodiment of the present invention will now be described. FIGS.1A through 1D and FIGS. 2A through 2C illustrate steps of producing apixel portion of an active matrix liquid crystal display to be describedin the present embodiment.

As shown in FIG. 1A, a silicon oxide film 102 having a thickness of 3000Å as a backing film is first formed on a glass substrate 101 using aplasma CVD process.

Next, an amorphous silicon film (not shown) is formed which will laterserve as a starting film made of a thin film semiconductor for formingan active later of a thin film transistor. The amorphous silicon film(not shown) is formed to a thickness of 500 Å using a plasma CVDprocess.

The amorphous silicon film is then crystallized using a heating processor irradiating it with laser beams or using a process which is acombination of the heating process and irradiation with laser beams toobtain a crystalline silicon film (not shown).

The crystalline silicon film (not shown) is patterned to obtain anactive layer 103 of a thin film transistor.

Next, a plasma CVD process is performed to form a silicon oxide film 104having a thickness of 1000 Å which serves as a gate insulation film bycovering the active layer 103 as shown in FIG. 1A. Thus, the state asshown in FIG. 1A is realized.

Next, an aluminum film (not shown) including 0.1% scandium by weight isformed to a thickness of 4000 Å using a sputtering process. Thisaluminum film will serves as a gate electrode later.

After forming the aluminum film, a dense anodic oxide film (not shown)is formed on the surface thereof to a thickness of 100 Å. Thisanodization is carried out by using the aluminum film as an anode in anelectrolyte obtained by neutralizing an ethylene glycol solutionincluding 3% tartaric acid with aqueous ammonia.

Further, patterning is performed by providing a resist mask (not shown).A gate electrode 105 is formed as a result of the patterning.

After the formation of the gate electrode 105, anodization is carriedout again with the resist mask (not shown) left in place. Thisanodization is carried out using an aqueous solution including 3% oxalicacid as an electrolyte.

This anodization selectively takes place only on side faces of the gateelectrode 105 because of the leftover resist mask (not shown). Theanodic oxide film formed in this step has a porous structure.

Thus, a porous anodic oxide film 106 is formed on the side faces of thegate electrode 105.

This porous anodic oxide film can be grown to a thickness on the orderof several μm. The size of this growth can be controlled by the durationof the anodization.

Here, the thickness of the anodic oxide film 106 is 6000 Å.

Next, anodization is carried out again using an electrolyte obtained byneutralizing an ethylene glycol solution including 3% tartaric acid withaqueous ammonia. In this anodizing step, since the electrolytepenetrates the porous anodic oxide film 106, a dense anodic oxide film107 is formed around the gate electrode 105.

The thickness of this dense anodic oxide film 107 is 500. The primaryfunction of this dense anodic oxide film 107 is to cover the surface ofthe gate electrode to prevent generation of hillocks and whiskers insubsequent steps.

It also has a function of protecting the gate electrode 105 so that itis not etched at the same time when the porous anodic oxide film 106 isremoved later.

It also has a function of contributing to formation of an offset gateregion which is formed later using the porous anodic oxide film 106 as amask.

Thus, the state as shown in FIG. 1B is realized.

In this state, impurity ions are implanted. P (phosphorus) ions areimplanted here to obtain an N-channel type thin film transistor.

When implantation of impurity ions is carried out in the state as shownin FIG. 1B, the impurity ions are selectively implanted in regionsindicated by 108 and 111. That is, the regions 108 and 111 become highdensity impurity regions.

The impurity ions are not implanted in a region 109 directly under thegate electrode 105 because the gate electrode 105 serves as a mask. Thisregion 109 serves as a channel formation region.

The impurity ions are not implanted also in a region indicated by 110because the porous anodic oxide film 105 and the dense anodic oxide film107 serve as a mask. The region indicated by 107 serves as an offsetgate region which functions neither as a source/drain region nor as achannel formation region.

Particularly, the offset gate region has a function of moderating thestrength of an electric field formed between the channel formationregion and the drain region. The presence of the offset gate regionallows the OFF current value of the thin film transistor to be reducedand suppresses deterioration of the same.

Thus, the source region indicated by 108, the channel formation regionindicated by 109, the offset gate region indicated by 110 and the drainregion indicated by 111 are formed on a self-alignment basis.

When the implantation of impurity ions is completed, the porous anodicoxide film 106 is selectively removed. Then, an annealing process isperformed by means of irradiation with laser beams. Since laser beamscan be directed to the vicinity of the interface between the highdensity impurity region and the offset gate region, the junction portionwhich has been damaged by the implantation of impurity ions can besufficiently annealed.

When the state as shown in FIG. 1B is realized, a silicon oxide film 112having a thickness of 2000 is formed as a first layer insulation film.

A silicon nitride film or a multi-layer film consisting of a siliconoxide film and a silicon nitride film may be used as this first layerinsulation film.

Next, a contact hole is formed in the first layer insulation film 112 toform a source electrode 113 which contacts with the source region of thethin film transistor. Thus, the state as shown in FIG. 1C is realized.

Then, a second layer insulation film 114 is formed using transparentpolyimide resin or acrylic resin. The layer insulation film 114 made ofa resin material is formed to have a flat surface. Thus, the state asshown FIG. 1D is realized.

Next, as shown in FIG. 2A, a chromium film is formed and patterned intoa masking film 115 which serves as a masking film and also as a blackmatrix for the thin film transistor.

A material having a relative dielectric constant equal to or smallerthan 3 is chosen as the resin material for forming the second layerinsulation film 114. The film is to be made as thick as several μm. Aresin material is advantageous for such an application because it doesnot prolong the time required for the production steps even when it ismade thick.

Such a configuration makes it possible to prevent generation of acapacity between the masking film 115 made of chromium and the thin filmtransistor located thereunder.

Further, the surface of the second layer insulation film 114 can beeasily flattened if it is formed from a resin material. This makes itpossible to prevent leakage of light originating from surfaceirregularity.

When the state as shown in FIG. 2A is realized, a third layer insulationfilm 116 is formed using a resin material, silicon oxide film, orsilicon nitride film. Here, the same resin material as for the secondlayer insulation film 114 is used for this third layer insulation film116.

The use of a resin material as the third layer insulation filmadvantageously solves the problem of generation of a capacity between apixel electrode to be formed later and the masking film 115 and flattensthe surface on which the pixel electrode is to be formed.

Thus, the state as shown in FIG. 2B is realized. Then, a pixel electrode117 is formed by forming a contact hole, forming an ITO electrode whichconstitutes the pixel electrode, and performing patterning.

This completes the configuration as shown in FIG. 2C. In theconfiguration shown in FIG. 2C, the layer insulation film providedbetween the thin film transistor (especially the source electrode 113)and the masking film (and/or black matrix) 115 can be formed to have asmall relative dielectric constant and a large thickness. This makes itpossible to prevent generation of an unnecessary capacity.

The configuration as described above can be realized because of the factthat the formation of a thick resin film is a simple industrial processwhich does not involve an increase in processing time as describedabove.

A second embodiment of the present invention will now be described.

The present embodiment is characterized in that it employs aconfiguration which is an improvement over the configuration describedin the first embodiment to provide higher reliability.

As described above, a metal material such as chromium is used for themasking film and black matrix. From the viewpoint of long termreliability, however, concern exists about dispersion of impurities fromthe metal material and a short-circuit between the metal material andother electrodes or wiring.

Especially, if there is a pin hole in the layer insulation film 116 inthe state as shown in FIG. 2C, a problem arises in that a short-circuitoccurs between the masking film 115 (which may simultaneously serve as ablack matrix) and the pixel electrode 117.

A possible method for eliminating the influence of a pin hole present inthe layer insulation film 116 is to form the layer insulation film 116as a special multi-layer film.

However, such a method is unfavorable because it can increase the numberof production steps and manufacturing cost.

A configuration according to the present embodiment addresses thissituation by employing a material which can be anodized for the maskingfilm for shading the thin film transistor and by forming an anodic oxidefilm thereon in the configuration described in the first embodiment.

Aluminum or tantalum may be used as the material which can be anodized.

Especially, the use of aluminum will provide a preferable masking filmbecause it allows the anodic oxide film to be colored in black or asimilar dark color utilizing an anodizing technique used for industrialproducts such as aluminum sashes.

FIGS. 3A through 3C schematically show production steps according to thepresent embodiment. First, the state as shown in FIG. 1D is realized bythe steps shown in FIGS. 1A through 1D. Then, a masking film 115 isformed as shown in FIG. 2A.

Here, aluminum is used as the masking film 115. Anodization is performedin an electrolyte to form an anodic oxide film 301 on the surface of themasking film 115 as shown in FIG. 3A.

FIG. 3A shows the masking film 301 as a masking film for shading a thinfilm transistor. However, it is normally extended further to also form ablack matrix.

When the state as shown in FIG. 3A is realized, a third layer insulationfilm 116 is formed by a silicon oxide film or silicon nitride film orformed from a resin material as shown in FIG. 3B.

Further, a pixel electrode 117 is formed using ITO as shown in FIG. 3C.

Even if a pin hole exists in the layer insulation film 116, the presenceof the anodic oxide film 301 prevents the pixel electrode 117 andmasking film 115 from being short-circuited.

In addition, since the anodic oxide film 301 is chemically stable, it ispreferable from the viewpoint of long term reliability in that it canprevent impurities in the masking film 115 from being dispersed in theneighborhood thereof.

A third embodiment of the present invention will now be described.

The present embodiment relates to a configuration in which an apertureratio of a pixel is improved. There is a general need for aconfiguration of a pixel that makes the aperture ratio as large aspossible. In order to obtain a large aperture ratio of a pixel, thepixel electrode must be provided to have an area which is as wide aspossible.

However, a severe limitation is placed on such an attempt in that if thepixel electrode overlaps the thin film transistor or wiring, a capacityis generated therebetween.

The present embodiment provides a configuration which reduces theproblem of generation of a capacity.

FIGS. 4A through 4C show steps of producing the configuration accordingto the present embodiment. The steps shown in FIGS. 4A and 4B are thesame as those in FIGS. 3A and 3B.

First, a masking film 115 made of aluminum is formed as shown in FIG.4A. An anodic oxide film indicated by 301 is formed on the surface ofthe masking film 115.

Further, a third layer insulation film 116 is formed as shown in FIG.4B. The layer insulation film 116 is formed from a resin material.

A pixel electrode 117 is then formed using ITO as shown in FIG. 4C. Thepixel electrode 117 is overlaid on the thin film transistor. Thismaximizes the aperture ratio of the pixel.

With the configuration as shown in FIG. 4C, layer insulation films 114and 116 can be formed from a resin material having a small relativedielectric constant (as compared to a silicon oxide film or siliconnitride film) with an increased thickness. This makes it possible toreduce the problem of a capacity as described above.

Further, the area of the pixel electrode can be increased to obtain alarger aperture ratio for the pixel.

Although a top gate type is employed for a thin film transistor in theforegoing embodiments, in this embodiment 4 is described a method formanufacturing a bottom gate type thin film transistor in which a gateelectrode is closer to a substrate than an active layer is.

The manufacturing steps in accordance with this embodiment 4 are shownin FIGS. 5(A) to 5(D). First, as shown in FIG. 5(A), a silicon oxidefilm 202 as a base film is formed on a glass substrate 201 bysputtering. Then, a gate electrode 203 is formed from aluminum.

In this gate electrode, scandium is contained in aluminum at 0.18 weight%. Concentration of other impurities should be made as low as possible.The foregoing is for suppressing formation of protrusion called hillockor whisker formed due to extraordinary growth of aluminum in thesubsequent step.

Then, a silicon oxide film 204 functioning as a gate insulating film isformed to a thickness of 500 Å by plasma CVD.

Then, an amorphous silicon film (to become a crystalline silicon film205 later) not shown in the drawings is formed by plasma CVD as astarting film for forming an active layer of a thin film transistor. Lowpressure thermal CVD may be used instead of plasma CVD.

Then, by a laser light irradiation, the amorphous silicon film not shownin the drawings is crystallized. A crystalline silicon film 205 is thenobtained. Thus, a structure shown in FIG. 5(A) is obtained.

After a structure shown in FIG. 5(A) is obtained, an active layer 206 isformed by conducting a patterning.

Then, a silicon nitride film not shown in the drawings is formed, and isshaped into a mask pattern 207 made of the silicon nitride film, byirradiating a light thereto from a rear surface side of the substrateusing the gate electrode.

The mask pattern 207 is formed as follows.

At first, a resist mask pattern is formed by light irradiation from arear surface side of the substrate 201 using the gate electrode pattern.Further, the resist mask pattern is retreated by ashing. A patterndesignated by a reference numeral 207 is obtained by patterning thesilicon nitride film using the retreated resist mask pattern not shownin the drawings. Thus, the structure shown in FIG. 5(B) is obtained.

Then, an impurity doping is conducted using the mask pattern 207. Forexample, P(phosphorus) is used as a dopant, and plasma doping is used asa doping method.

In this step, regions 208 and 209 are doped with P. A region 210 is notdoped with P.

After completion of the doping, a laser light irradiation is conductedfrom above to conduct activation of the doped regions and to conductannealing of damages caused due to impact of the dopant ions.

Thus, as shown in FIG. 5(C), a region 208 is formed as a source region.Also, a region 209 is formed as a drain region. Also, a region 210 isformed as a channel region.

Then, a silicon nitride film is formed as a first interlayer insulatingfilm 211 to a thickness of 2000 Å by plasma CVD.

A silicon oxide film, silicon oxinitride film, or a multi-layer filmcomprising a silicon oxide film and a silicon nitride film (any one ofthem can be formed on the other) can be used instead of the siliconnitride single film, as the first interlayer insulating film usedherein.

Then, a contact hole is formed for the source region 208 in the firstinterlayer insulating film 211, and a source electrode is formed toprovide a contact to the source region 208. Thus, the structure shown inFIG. 5(C) is obtained.

Then, as shown in FIG. 5(D), a second interlayer insulating film 213having a flat surface is formed from a transparent polyimide resin oracrylic resin. For example, a spin coating can be employed as a filmformation method.

Then, a chromium film is formed on the second interlayer insulating film213, and is patterned to form a light-shielding film 214 which serves asboth a light-shielding film and a black matrix for a thin filmtransistor. Then, a third interlayer insulating film 215 is formed fromthe same resin material film as the second interlayer insulating film213.

A contact hole which reaches the drain region 209 is formed in the firstto third interlayer insulating films 211, 213, 215. Then, ITO (indiumtin oxide) film is formed on a surface of the third interlayerinsulating film 215, and is patterned into a pixel electrode 216.

A thin film transistor shown in FIG. 5(D) is completed through theforegoing steps.

Using the invention disclosed in this specification, an effectivemasking film can be provided in a configuration of a pixel of an activematrix display, and an active matrix display having high performance canbe configured. The invention disclosed in this specification isapplicable not only to active matrix liquid crystal displays but also toEL type displays and the like of the active matrix type.

While particular embodiments of the present invention have been shownand described, it will be obvious to those skilled in the art thatchanges and modifications may be made without departing from thisinvention in its broader aspects and, therefore, the appended claims areto encompass within their scope all such changes and modifications asfall within the true spirit and scope of this invention.

What is claimed is:
 1. An active matrix electro-luminescent displaycomprising: a thin film transistor provided over a substrate andcomprising a gate electrode, a gate insulating film provided over saidgate electrode, a source region, a drain region, a channel regionprovided between said source region and said drain region and over saidgate insulating film; an insulating film comprising silicon nitrideprovided over said thin film transistor; a transparent insulating filmprovided over said insulating film to provide a leveled upper surfaceover said thin film transistor; a pixel electrode provided over saidtransparent insulating film and connected with said thin filmtransistor; and a black matrix comprising a metal covering at least apart of a peripheral region of said pixel electrode.
 2. An active matrixelectro-luminescent display comprising: a thin film transistor providedover a substrate and comprising a gate electrode, a gate insulating filmprovided over said gate electrode, a source region, a drain region, achannel region provided between said source region and said drain regionand over said gate insulating film; a first insulating film comprisingsilicon oxynitride provided over said thin film transistor; a secondinsulating film provided over said first insulating film to provide aleveled upper surface over said thin film transistor; a pixel electrodeprovided over said second insulating film and connected with said thinfilm transistor; and a black matrix comprising a metal covering at leasta part of a peripheral region of said pixel electrode.
 3. An activematrix electro-luminescent display comprising: a thin film transistorprovided over a substrate and comprising a gate electrode, a gateinsulating film provided over said gate electrode, a source region, adrain region, a channel region provided between said source region andsaid drain region and over said gate insulating film; an insulating filmcomprising silicon nitride provided over said thin film transistor; atransparent organic resin film provided over said insulating film toprovide a leveled upper surface over said thin film transistor; a pixelelectrode provided over said transparent organic resin film andconnected with said thin film transistor; and a black matrix comprisinga metal covering at least a part of a peripheral region of said pixelelectrode.
 4. An active matrix electro-luminescent display according toclaim 3, wherein said transparent organic resin film comprises polyimideresin or acrylic resin.
 5. An active matrix electro-luminescent displayaccording to claim 3, wherein said pixel electrode comprises indium tinoxide.
 6. An active matrix electro-luminescent display comprising: athin film transistor provided over a substrate and comprising a gateelectrode, a gate insulating film provided over said gate electrode, asource region, a drain region, a channel region provided between saidsource region and said drain region and over said gate insulating film;an insulating film comprising silicon oxynitride provided over said thinfilm transistor; an organic resin film provided over said insulatingfilm to provide a leveled upper surface over said thin film transistor;a pixel electrode provided over said organic resin film and connectedwith said thin film transistor; and a black matrix comprising a metalcovering at least a part of a peripheral region of said pixel electrode.7. An active matrix electro-luminescent display according to claim 6,wherein said organic resin film comprises polyimide resin or acrylicresin.
 8. An active matrix electro-luminescent display according toclaim 6, wherein said pixel electrode comprises indium tin oxide.
 9. Anactive matrix electro-luminescent display comprising: a thin filmtransistor provided over a substrate and comprising a gate electrode, agate insulating film provided over said gate electrode, a source region,a drain region, a channel region provided between said source region andsaid drain region and over said gate insulating film; an insulating filmcomprising silicon nitride provided over said thin film transistor; atransparent organic resin film provided over said insulating film toprovide a leveled upper surface over said thin film transistor; a pixelelectrode provided over said transparent organic resin film andconnected with said thin film transistor; and a masking film comprisinga metal for shading said thin film transistor.
 10. An active matrixelectro-luminescent display according to claim 9, wherein saidtransparent organic resin film comprises polyimide resin or acrylicresin.
 11. An active matrix electro-luminescent display according toclaim 9, wherein said pixel electrode comprises indium tin oxide.
 12. Anactive matrix electro-luminescent display comprising: a thin filmtransistor provided over a substrate and comprising a gate electrode, agate insulating film provided over said gate electrode, a source region,a drain region, a channel region provided between said source region andsaid drain region and over said gate insulating film; an insulating filmcomprising silicon oxynitride provided over said thin film transistor;an organic resin film provided over said insulating film to provide aleveled upper surface over said thin film transistor; a pixel electrodeprovided over said organic resin film and connected with said thin filmtransistor; and a masking film comprising a metal for shading said thinfilm transistor.
 13. An active matrix electro-luminescent displayaccording to claim 12, wherein said organic resin film comprisespolyimide resin or acrylic resin.
 14. An active matrixelectro-luminescent display according to claim 12, wherein said pixelelectrode comprises indium tin oxide.
 15. An active matrixelectro-luminescent display comprising: a thin film transistor providedover a substrate and comprising a gate electrode, a gate insulating filmprovided over said gate electrode, a source region, a drain region, achannel region provided between said source region and said drain regionand over said gate insulating film; a first insulating film comprisingsilicon nitride provided over said thin film transistor; a secondinsulating film comprising an organic resin film provided over saidfirst insulating film to provide a leveled upper surface over said thinfilm transistor; a conductive layer formed over said second insulatingfilm; a third insulating film comprising an organic resin film over saidsecond insulating film and said conductive layer; and a pixel electrodeprovided over said third insulating film and electrically connected withsaid thin film transistor.
 16. An active matrix electro-luminescentdisplay according to claim 15, wherein said organic resin film comprisespolyimide resin or acrylic resin.
 17. An active matrixelectro-luminescent display according to claim 15, wherein said pixelelectrode comprises indium tin oxide.
 18. An active matrixelectro-luminescent display according to claim 15, the pixel electrodeis directly connected to said thin film transistor.
 19. An active matrixelectro-luminescent display comprising: a thin film transistor providedover a substrate and comprising a gate electrode, a gate insulating filmprovided over said gate electrode, a source region, a drain region, achannel region provided between said source region and said drain regionand over said gate insulating film; a first insulating film comprisingsilicon oxynitride provided over said thin film transistor; a secondinsulating film comprising an organic resin film provided over saidfirst insulating film to provide a leveled upper surface over said thinfilm transistor; a conductive layer formed over said second insulatingfilm; a third insulating film comprising an organic resin film over saidsecond insulating film and said conductive layer; and a pixel electrodeprovided over said third insulating film and electrically connected withsaid thin film transistor.
 20. An active matrix electro-luminescentdisplay according to claim 19, wherein said organic resin film comprisespolyimide resin or acrylic resin.
 21. An active matrixelectro-luminescent display according to claim 19, wherein said pixelelectrode comprises indium tin oxide.
 22. An active matrixelectro-luminescent display according to claim 19, the pixel electrodeis directly connected to said thin film transistor.
 23. An active matrixelectro-luminescent display comprising: a thin film transistor providedover a substrate; a first insulating film comprising silicon nitrideprovided over said thin film transistor; a second insulating filmcomprising an organic resin film provided over said first insulatingfilm to provide a leveled upper surface over said thin film transistor;a conductive layer formed over said second insulating film; a thirdinsulating film comprising an organic resin film over said secondinsulating film and said conductive layer; and a pixel electrodeprovided over said third insulating film and electrically connected withsaid thin film transistor.
 24. An active matrix electro-luminescentdisplay according to claim 23, wherein said organic resin film comprisespolyimide resin or acrylic resin.
 25. An active matrixelectro-luminescent display according to claim 23, wherein said pixelelectrode comprises indium tin oxide.
 26. An active matrixelectro-luminescent display according to claim 23, the pixel electrodeis directly connected to said thin film transistor.
 27. An active matrixelectro-luminescent display comprising: a thin film transistor providedover a substrate; a first insulating film comprising silicon oxynitrideprovided over said thin film transistor; a second insulating filmcomprising an organic resin film provided over said first insulatingfilm to provide a leveled upper surface over said thin film transistor;a conductive layer formed over said second insulating film; a thirdinsulating film comprising an organic resin film over said secondinsulating film and said conductive layer; and a pixel electrodeprovided over said third insulating film and electrically connected withsaid thin film transistor.
 28. An active matrix electro-luminescentdisplay according to claim 27, wherein said organic resin film comprisespolyimide resin or acrylic resin.
 29. An active matrixelectro-luminescent display according to claim 27, wherein said pixelelectrode comprises indium tin oxide.
 30. An active matrixelectro-luminescent display according to claim 27, the pixel electrodeis directly connected to said thin film transistor.